Formlabs Clear Resin V5 Form 4, 5L

Formlabs Clear Resin V5 Form 4, 5L

Maximize your production throughput with the bulk-sized Formlabs Clear Resin V5 Form 4, 5L container. Engineered specifically for the high-speed Form 4 ecosystem, this advanced general-purpose resin combines rigidity and precision with exceptional optical transparency. It is the ultimate solution for manufacturing clear parts, light pipes, and fluidic devices at unprecedented speeds.
Important: This 5L container requires a Resin Pump for operation. Please note that items of this volume are made to order and typically have a lead time exceeding 5 weeks.

Why Choose Clear Resin?

Clear Resin V5 is a stiff and strong material designed to balance rapid print speeds with superior dimensional accuracy. It is the go-to choice for applications requiring translucency or visibility of internal components.

Crystal-Clear Transparency

Produce parts that look like glass or polished acrylic. With standard post-processing, Clear Resin V5 achieves near-optical transparency. The V5 formulation eliminates the yellow tint of older resins, offering a completely neutral, clear finish for professional-grade prototypes and end-use parts.

Unmatched Print Speed

Take full advantage of the Form 4's capabilities. This resin is formulated to print three times faster than the previous V4 generation, allowing for rapid design iteration and high-volume manufacturing without compromising on surface quality or detail.

Flawless Surface Finish

Experience smooth, injection-mold-like surfaces right off the printer. The resin's formulation minimizes layer lines, making it perfect for optical components, lenses, and presentation models where visual fidelity is critical.

Key Engineering Applications

Clear Resin V5 is a versatile tool for designers and engineers, excelling in:

• Optics: Custom lenses, prisms, light guides, and LED diffusers.
• Fluidics: Millifluidic channels, manifolds, and mixing devices.
• Visual Prototypes: Clear enclosures, housings, and models that showcase internal mechanisms.
• Tooling: Durable molds and dies that simulate polycarbonate properties.

Technical Specifications and Mechanical Data

General Properties:

• Technology: SLA
• Application: General Purpose
• Material Classification: Stiff & Strong

Mechanical Performance:

The material properties vary based on the post-curing process. See the data below for two standard workflows:

Workflow 1: Post-cured at Room Temperature for 5 Minutes

• Ultimate Tensile Strength: 51 MPa
• Tensile Modulus: 2575 MPa
• Elongation at Break: 10%
• Flexural Strength: 92 MPa
• Flexural Modulus: 2450 MPa
• Notched Izod: 29 J/m
• Heat Deflection Temperature @ 0.45 MPa: 56 °C

Workflow 2: Post-cured at 60 °C for 15 Minutes (Recommended for Max Strength)

• Ultimate Tensile Strength: 60 MPa
• Tensile Modulus: 2750 MPa
• Elongation at Break: 8%
• Flexural Strength: 105 MPa
• Flexural Modulus: 2700 MPa
• Notched Izod: 29 J/m
• Heat Deflection Temperature @ 0.45 MPa: 74 °C

Why Purchase from 3DPrinter?

As official Formlabs partners, we provide the best pricing, a full manufacturer's warranty, and dedicated service support. Our team of experts, with industry experience since 2012, is here to offer professional advice and assist with your selection. We provide qualified support before, during, and after your purchase to ensure your success. Shop with the experts at 3DPrinter.